Abstract
Explosion welding of cooper C10200 to AW 5083 aluminium alloy was performed. The C10200 was proposed as a flyer plate. A parallel setup was used during explosive welding. Bimetals were characterized by regular wavy interface. The intermetallic compound (IMC) layer was observed at the interface of bimetals after 12 month, however, no annealing was performed. EDX analyses revealed that the interface layer consists of the intermetallic compound CuAl. Microhardness at the interface increased due to the presence of the IMC and work hardening as well.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: Materiały Wysokoenergetyczne / High Energy Materials
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.