Abstract

The TiCN coatings were successfully prepared by means of reactive plasma with spraying self-made composite powder prepared from 150°C to 350°C in the paper. Sucrose was used as a carbon source, using the means of Precursor body carbon, sucrose and titanium powder mixing at high temperature after the heat treatment furnace for carbonization. Finally, the titanium powder was wrapped by the carbon, so the composite powder was mixed more uniform and could react more fully. TiCN coatings could not be synthesized with the composite powder prepared the temperatures of 150°C and 250°C, because the sucrose was not carbonized totally and could not carbonize to synthesize TiCN with Ti and N2 in the process of spraying. TiCN coatings were prepared by spraying the composite powder under heat treatment at 350°C and which composed of Ti and C at a ratio of 1:3. The phase compositions, the morphologies, the hardness and the microstructures were analyzed. The results showed that TiCN coating was consisted of TiC0.2N0.8 phase and a few of TiN, the hardness of TiCN coating could reach 1000HV, the friction coefficient is about 0.45, the wear resistance of TiCN coating was lower compared with TiC coating because of the looser structure and the lower hardness.

Talk to us

Join us for a 30 min session where you can share your feedback and ask us any queries you have

Schedule a call

Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.