Abstract
ABSTRACTDensification behaviours of 17-4PH stainless steel powders (SUS17-4PH) of three different particle sizes during the sintering were investigated. The samples with different mean particle sizes of 3.17, 4.22 and 8.30 µm were prepared through powder-binder mixing, injection moulding, and solvent and thermal debindings. The in situ shrinkage data measured by dilatometry tests were treated to analyse the densification behaviour of each sample. In order to characterise the densification behaviour with a minimum set of experiments, the master sintering curve (MSC), as well-known and straight-forward approach, was employed. After constructing the MSCs for powders of different particle sizes, the effects of particle size on the densification were analysed in many respects including shrinkage, strain rate, apparent activation energy, and work of sintering.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.