Abstract
Multi-layers of Co20Fe60B20 and Pt with large perpendicular magnetic anisotropies (PMA), comparable to those obtained with the more widely utilized Ta/CoFeB/MgO heterostructures, are reported. CoFeB thickness of approximately 0.8nm is necessary to maximize PMA in Pt/CoFeB/Pt. Strong PMA can only be obtained upon careful tuning of the material the CoFeB layer is deposited on. Specifically, a Pt layer thickness of at least 3nm is necessary to obtain PMA in CoFeB due to the emergence of (111) texture in thicker Pt films. The absence of a magnetic dead layer at the interface between CoFeB and Pt (as opposed to an interface between CoFeB and Ta) maximizes the amount of magnetic content per unit volume. Furthermore, this study investigates the magnetic properties of multi-layer structures where four CoFeB layers are deposited between Pt and Pt/Ta/Pt buffers. While the out-of-plane remanent magnetization of the structures is low, they present small nucleation field down to 30Oe and large anisotropy energy in the range of 106erg/cc.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.