Abstract
AbstractEu‐doped transparent oxyfluoride aluminosilicate glass was prepared by controlling with Al codoping of melt‐quenched glass fabricated under air atmosphere. In the presence of Al input, the photoluminescence emission spectra under 393 nm excitation shows a blue shift by adjusting the ratio of Eu3+ and Eu2+. After heat treatment of glass, the ratio of Eu3+ and Eu2+ of luminescence emission were changed by controlling treatment temperature. The PL intensity of Eu3+ and Eu2+ ions in the glass‐ceramics (GC) was much stronger than in the precursor glass (PG). The possible mechanism responsible for color tuneability of the ratio of Eu3+ and Eu2+ doped was discussed.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.