AbstractIn this study, we fabricated Mg2Si from metal Mg and Si with different particle sizes (425 - 300, 300 - 180, and 75 μm or less) using spark plasma sintering (SPS) equipment. Additionally, the Mg2Si formation was investigated. A sieved Si powder was mixed with metal Mg powder in an inert gas (Ar) atmosphere. The mixture was placed in a graphite die while still in an Ar atmosphere and subjected to SPS at 923 K and 1113 K. The obtained sintering bodies were Mg2Si particles with a size of about 5 μm. Then, the sintered bodies were evaluated by X-ray diffraction (XRD). As a result, it was confirmed that generation of Mg2Si increased with decreasing Si particle size.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.