Abstract
The purpose of this study was to obtain dental ceramic materials with excellent mechanical properties and high resistance to low temperature degradation (LTD) via stereolithography (SLA) in combination with microwave sintering (MWS). The results have shown that the unaged MWS-1425 °C 3Y-TZP ceramics with uniform microstructure have high density up to 99.04% and excellent mechanical properties (Vickers hardness 14.07 GPa, fracture toughness 4.32 MPa m1/2, flexural strength 947.87 MPa). After 50 h of LTD, the m-phase content of MWS 3Y-TZP ceramics accounts for only 10.3%. In addition, the surface roughness increases by only 1.3 nm, the degraded depth is less than 5 μm, and the flexural strength exceeds 900 MPa. This exhibits the high resistance to LTD and excellent mechanical properties of dental 3Y-TZP ceramics can be obtained.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: Journal of the Mechanical Behavior of Biomedical Materials
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.