Abstract
ABSTRACTThe Na0.96Li0.04NbO3 ceramic solid solution was prepared by means of a two-stage hot-pressing technology. The X-ray diffraction analysis showed the formation of a single perovskite phase with an orthorhombic symmetry in the investigated composition. The microstructure and EDS measurements were performed. They confirmed the high purity and the expected qualitative composition. A good homogeneity of the microstructures and a small degree of porosity were observed. The elastic modulus (the Young's modulus E, shear modulus G, and Poisson's ratio ν) of Na0.96Li0.04NbO3 were determined with the use of an ultrasonic method. The electrical properties of Na0.96Li0.04NbO3 ceramics were investigated at the frequency ranging from 0.5 kHz to 200 kHz, and the temperature ranging from room temperature to 750 K. The test sample shows a dielectric dispersion.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.