Abstract
In this study, magnetization and neutron diffraction of anti-ThCr2Si2-type Tb2O2Bi polycrystals were measured at various temperatures. The magnetization cusp at 11.1 K was confirmed to correspond to antiferromagnetic ordering with a propagation vector of [0.5 0.5 0]. In addition, a metamagnetic behavior was observed below 5.0 K. The metamagnetic behavior could be attributed to the incommensurate magnetic structure with an anomaly at 5.0 K.
Highlights
RE2O2Bi has attracted attention because of its electrical properties such as metal-insulator transition and superconductivity.10–15 the magnetic properties of RE2O2Bi were investigated by only magnetic susceptibility measurements, suggesting antiferromagnetic transition in RE2O2Bi (RE = Pr, Gd, Er)
Metamagnetic behavior was observed below 5.0 K, probably associated with anomalies at 5.0 K of the magnetic susceptibility and the incommensurate peak of neutron diffraction
Tb (99.9%), Tb4O7 (99.9%), and Bi (99.9%) powders were pelletized under 20 MPa in a nitrogen-filled glove box after mixing, where the nominal compositions were Tb2O1.6Bi1.4 and Tb2O1.5Bi1.5 for magnetization measurement and powder neutron diffraction, respectively
Summary
Magnetization and neutron diffraction of anti-ThCr2Si2-type Tb2O2Bi polycrystals were measured at various temperatures. The metamagnetic behavior could be attributed to the incommensurate magnetic structure with an anomaly at 5.0 K.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.