Abstract
Carbon/carbon (C/C)-SiC composite materials have a series of outstanding advantages, such as a light weight, resistance to thermal degradation, excellent friction performance, and good stability in complex environments. In order to improve the wear resistance of the C/C-SiC composite matrix, Si/SiC coatings were prepared by a combination of chemical vapor infiltration and reactive sintering. The wear performance of Si/SiC coatings with different amounts of silicon carbide was investigated. When the carbon silicon ratio in the slurry was 1:3, the SiC particle content in the coating was 93.0 wt.%; the prepared Si/SiC coating exhibited the lowest wear rate of 3.2 × 10−3 mg·N−1·m−1 among the four coatings; and its frictional coefficient was 0.95, which was higher than that of the substrate. As the residual Si content in the coating decreased, the continuity between SiC particles in the coating was improved. Both the high hardness of SiC and the dense coating contributed significantly to enhancing the coating’s wear resistance.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.