Abstract
Electrophoretic deposition (EPD) is a promising method for coating complex shaped interconnects and contact components for solid oxide fuel cells and electrolyzers. In this work, we employ a combination of finite element modelling and experiments to assess the effect of substrate curvature on the fabrication of a Mn1.5Co1.5O4 coating by EPD. The coating is deposited on steel substrates machined to create a well-defined curvature and on a Crofer 22 H steel grid. We find that post-deposition sintering of the coated steel substrate may lead to crack formation in concave surfaces, while a defect-free coating is achieved at convex surfaces. The formation of cracks is found to depend on a complex interplay between the coating thickness, the sintering procedure, and the substrate curvature radius. Oxidation testing in air at 750 °C showed that the Mn1.5Co1.5O4 coating reduced the oxidation rate of the Crofer 22 H steel grid. Sintering the coating by a two-step reduction and re-oxidation procedure resulted in a more protective coating showing a greater tendency for crack healing compared to sintering the coating in air only.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.