Abstract
Ga-doped ZnO (GZO) transparent conducting films were deposited on sapphire (0001) substrates using dual ion beam sputtering deposition system. The impact of growth temperature on the structural, morphological, elemental, optical, and electrical properties was thoroughly investigated and reported. X-ray diffraction measurements explicitly confirmed that all GZO films had (002) preferred crystal orientation. The film deposited at 400 °C exhibited the narrowest full-width at half-maximum value of 0.24° for (002) crystalline plane and the lowest room temperature electrical resistivity of 4.11 × 10−3 Ω cm. The Raman spectra demonstrated the vibrational modes at 576 and 650–670 cm−1, associated with native oxygen vacancies and elemental Ga doping in ZnO lattice, respectively. All doped films showed an overall transmittance of above 95 % in the visible spectra. A correlation between structural, optical, elemental, and electrical properties with GZO growth temperature was established.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have