Abstract
The change of the degree of order with increasing rolling reduction was determined by X-ray diffraction. During a subsequent isochronal annealing treatment between 273 K and 1473 K of 40% rolled samples, hardness, yield-stress and the intensities of the superlattice reflections were measured and the microstructural evolution was investigated by TEM. The correlation between the measured property changes are discussed.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.