Abstract
AbstractHigh‐temperature vulcanized silicone rubber was prepared by using allyl‐capped carbosilane dendrimers, in which the core molecules were Si(CH2CHCH2)4 and Ph2Si(CH2CHCH2)2 as crosslinker and nanoscale reinforcing filler, respectively. Allyl‐capped carbosilane dendrimers improved the mechanical properties of silicone rubber. The optimum tensile strength and tear strength were 9.6 MPa and 31.0 kN/m, respectively, when using SiGn(allyl)m as the crosslinker and 10.1 MPa and 32.0 kN/m, respectively, when using Ph2SiGn(allyl)m as the crosslinker. © 2006 Wiley Periodicals, Inc. J Appl Polym Sci 100: 1772–1775, 2006
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.