Abstract
A urethane methacrylate monomer, 2-[(butylcarbamoyl)oxy]ethyl methacrylate (BEM), methyl methacrylate (MMA), and butyl acrylate (BA) were used to prepare latexes. The effects of polymer process (batch versus semi-batch), polymer composition, and the locus (core-shell) of urethane functionality in the latex particles were studied. Urethane functional latexes were evaluated by FT-IR, solid state nuclear magnetic resonance (SS-NMR), dynamic light scattering (DLS), gas chromatography (GC), differential scanning calorimetry (DSC), tensile and dynamic mechanical thermal analysis (DMTA). A compositional drift was observed for the batch polymerization which resulted in early formed polymers rich in MMA and BEM. This accounted for the higher modulus and tensile strength in latexes derived from batch polymerization. Both homogeneous and core-shell structures were prepared. The tensile modulus, tensile strength and elongation-at-break were all dependent on BEM content.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.