Abstract
Mechanical testing of solvent cast films consisting of short-chain-length (SCL) polyhydroxyalkanoate (PHA) films suggested that films consisting of block copolymers retained more elasticity over time with respect to films of similar random copolymers of comparable composition. Two experimental techniques, wide angle X-ray scattering (WAXS) and uniaxial extension, were used to quantitatively investigate the structure–property relationship of bacterially synthesized PHA block copolymers of poly(3-hydroxybutyrate) (PHB) homopolymer and poly(3-hydroxybutyrate- co-3-hydroxyvalerate) random copolymer (PHBV) segments. Uniaxial testing experiments yielded the Young's modulus, ultimate tensile strength, and the elongation until fracture of the films. Percent crystallinity was determined by deconvolution of amorphous and crystalline scattering peaks obtained from WAXS. Two PHBV films containing either 8% 3-hydroxyvalerate monomer (3HV) or 29% 3HV exhibited a quick transition to brittle behavior, decreasing to less than 20% percent elongation at fracture within a few days after annealing. Conversely, the block copolymer samples remained higher than 100% elongation at fracture a full 3 months after annealing. Because block copolymers covalently link polymers that would otherwise form thermodynamically separate phases, the rates and degrees of crystallization of the block copolymers are less than the random copolymer samples. These differences translate into materials that extend the property space of biologically synthesized SCL PHA.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.