Abstract
Stress corrosion cracking behaviour of API-5L-X52 steel under cathodic protection in near-neutral and high pH conditions was studied using slow strain rate test method and electrochemical measurements. The slow strain rate test showed ductile and brittle fracture feature at low and high applied potentials, respectively. In order to identify the mechanism contributes in stress corrosion cracking; the electrochemical potentiodynamic polarisation test was done at fast and slow sweep rate. The results revealed that at near-neutral pH condition the anodic dissolution at crack tip was the dominant mechanism. While at high pH medium, the hydrogen based mechanism was dominant.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.