Abstract
Wire and arc additive manufacturing (WAAM), recognized for its capability to fabricate large-scale, complex parts, stands out due to its significant deposition rates and cost-effectiveness, positioning it as a forward-looking manufacturing method. In this research, we employed two welding currents to produce samples of 316 austenitic stainless steel utilizing the Cold Metal Transfer wire arc additive manufacturing process (CMT-WAAM). This study initially evaluated the maximum allowable arc travel speed (MAWFS) and the formation characteristics of the deposition bead, considering deposition currents that vary between 100 A and175 A in both CMT and CMT pulse(CMT+P) modes. Thereafter, the effect of the CMT+P mode arc on the microstructure evolution was analyzed using the EBSD technique. The findings indicate that the arc travel speed and deposition current significantly affect the deposition bead's dimensions. Specifically, an increase in travel speed or a reduction in current results in reduced bead width and height. Moreover, the employment of the CMT+P arc mode led to a reduction in the average grain size in the mid-section of the sample fabricated by CMT arc and wire additive manufacturing, from 13.426 μm to 9.429 μm. Therefore, the components of 316 stainless steel produced through the CMT+P-WAAM method are considered fit for industrial applications.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.