Abstract
Macroalgae with nontoxicity, biodegradability and biocompatibility has attracted more attentions as a sustainable alternative towards petroleum-derived plastics. However, brittleness and high affinity towards water has limited marine-based macroalgae films to be widely used. Thus, this paper aims to compare the roles of calcium chloride as ionic cross-linker and acrylic resin as covalent cross-linker in agar-PEG plasticised biofilm composite. Agar biofilm composite with PEG 1000 40% were cross-linked with i) calcium chloride 1, 2, 3 and 4 (CaCl2/agar) wt/wt % at 2 or 4 min immersion time, and ii) acrylic resin at 10, 20, 30, 40 and 50 (acrylic resin/agar) wt/wt %. FTIR and TGA proved that CaCl2 and acrylic resin managed to cross-link agar-PEG films ionically and covalently respectively. In general, films cross-linked with CaCl2 produced highest affinity towards water than films cross-linked with acrylic resin. Highest tensile strength, highest tensile modulus and lowest elongation at break was achieved when films cross-linked with CaCl2. Films cross-linked with CaCl2 has higher degradation rate than films cross-linked with acrylic resin. In conclusion, different mode of cross-linking (ionic or covalent) imparted different properties on the agar-PEG film.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.