Abstract
Pre-damage and undetected micro-defects in fiber-reinforced polymer (FRP) composites are significant challenges compromising the integrity and mechanical performance of composite structures in aerospace applications. To address this challenge, this experimental study investigated the low velocity impact (LVI) and compression after impact (CAI) behaviors of carbon fiber/epoxy (CF/E) reinforced with 0.0 (control sample), 0.2, and 0.4 wt% helical multiwalled carbon nanotubes (HMWCNTs). The LVI test results showed that the control samples, with epoxy as the predominant phase, registered the lowest peak force compared to the 0.2 wt and 0.4 wt% HMWCNT/epoxy composite laminates. The CAI test results showed a decrease in strength with increased impact energy and an increase in the weight percent of HMWCNTs. Consequently, the 0.4 wt% HMWCNT ladened composites could withstand higher load without undergoing significant deformations, exhibiting the highest impact resistances due to the presence of CNTs, which function as load-bearing material. The HMWCNT interleaved CF/E composite laminate samples subjected to 25 J of impact energy achieved a higher maximum force of 9870.25 N compared to 8527.26 N for the damaged samples at the same level of impact energies. This fact indicates that the damaged samples could not withstand sufficiently high impact forces due to local instability arising from existing damages. The results strongly suggest a high potential for HMWCNTs CF/epoxy laminate composites in making structural and substructural components in aircraft and automobiles due to their proven superior properties.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.