Intrinsic grain size, its distribution and magnetic properties due to the addition of B on CoCrPtB recording magnetic layer are studied for various B compositions (0–10 at. %). CoCrPtB films were grown on large CrMo grains with an average grain size of ∼27 nm in order to obtain the intrinsic grain structure of the B containing magnetic layer, maintaining good Co (1120) crystallographic texture. Remarkable reduction in average intrinsic grain diameter is observed from ∼24 to ∼6.9 nm as the B concentration was varied from 0 to 10 at. %, respectively, on CoCrPt. The presence of B both within and outside the ferromagnetic phase is suggested to explain the observed coercivity dependence in CoCrPtB systems.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.