Abstract
We report on the structural, magnetic and electronic properties of Rh substituted LaNiO3, LaNi1–xRhxO3 (0 ≤ x ≤ 1). Increased Rh contents are associated with increased structural distortion, and we observe a phase transformation and an immiscibility gap between 0.15 ≤ x ≤ 0.25, separating the R-3c and Pnma perovskite structure regimes. Structural evaluation by synchrotron X-ray diffraction, X-ray absorption spectroscopy and DC magnetic measurements suggest variations in oxidation state for the B-site cations, with Ni(II)/Rh(IV), in addition to Rh(III), dominating for high Rh-contents. Although ordering of Ni(II)/Rh(IV) is possible, no B-site ordering between Ni and Rh is observed for any composition. A metal-to-insulator transition occurs upon Rh-substitution, correlating with the structural transition. DC- and AC magnetic measurements reveal that several of the compositions are magnetically frustrated with both antiferro- and ferromagnetic behaviour at low temperatures. The antiferromagnetic interactions are dominating, while the ferromagnetic interactions increase with increasing Rh-content, to a maximum at x = 0.80 and x = 0.90 in LaNi1–xRhxO3. The mixed valence states are assumed to contribute with a ferromagnetic super-exchange interaction between Ni(II) and Rh(IV).
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.