Abstract
The acid-catalysed cure reaction of a phenolic resin at 80°C results in the trapping of water as micron-sized spherical domains within the resin. When untreated commercial ultra-high modulus polyethylene (UHMPE) fibre is used as reinforcement with this resin, the water is trapped at the interface due to the poor wet-out of the fibre by the resin. This produces low interfacial shear strengths. A short radio frequency plasma treatment of the fibre in oxygen or water increases the shear strength by more than a factor of 2. The water liberated on resin cure is not trapped at the interface of the plasma-treated fibres, due to the enhanced wet-out of the fibre by the phenolic resin prior to cure. The plasma-treated UHMPE shows surface restructuring by XPS over a period of a week, but there is no loss of interfacial shear strength when the phenolic composite is fabricated, consistent with rapid reorientation of the carbonyl and carboxyl functionality in the presence of the resin.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.