Abstract
The need for high strength hydrogels in load bearing applications has motivated an effort to improve the mechanical properties of these soft and wet materials. However, hydrogels with high strength, excellent elasticity and fatigue resistance are rarely reported. In this study, we fabricated hydrogels with excellent comprehensive mechanical performances by copolymerization of 2-vinyl-4,6-diamino-1,3,5-triazine (VDT) and chain length modulable polyethylene glycol diacrylates (PEGDA). The intermolecular hydrogen bonding effects from diaminotriazine were shown to increase both the tensile and compressive strengths of the gels up to MPa levels, and longer PEG chains could increase the gel's elongation to over 700%. The stress-softening phenomenon did not appear until the VDT content in all the hydrogels was above 50 wt%. PEG35K-PVDT gel containing 93 wt% water was able to resist car pressing and retain excellent fatigue resistance during 20 000 cycles of compression due to hydrogen bonding reinforcing effect and effective energy dissipation of flexible polyethylene glycol chains. These high strength and elastic hydrogels with antifatigue ability may serve as soft tissue engineering scaffolds.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.