Abstract
ABSTRACTIn recent decades, flax fibre has become a popular natural resource as reinforcement in polymeric composites. However, the pure mode characterisation of flax fibre composites is rather limited. Furthermore, the mixed-mode delamination is not yet available. Nevertheless, delamination behaviour is important to be characterised as it is a major problem in composite laminates. This study examined the delamination behaviour of a woven flax/epoxy composite. Specimens were tested using mode I double cantilever beam, mode II end-notched flexure and mixed-mode I+II single leg bending tests. Results showed that the mode I, mode II and mixed-mode I+II fracture toughness were 363.23, 962.17 and 649.06 N m−1, respectively. When the fracture toughness values were fitted using Benzeggagh–Kenane criterion, it was found that the best-fit material parameter η was attained at 0.88. This information is useful to estimate the variation of fracture toughness with the mode ratio. Finally, through scanning electron micrographs, it was noticed that fibre/matrix debonding was the major fracture mechanism in all loading modes. In conclusion, the findings from this study suggested that the composite was suitable to be used for structural applications under mixed-mode loading.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.