Abstract
The interfacial properties of the Co2FeAl0.5Si0.5/MgO based magnetic tunnel junction have been investigated using x ray absorption spectroscopy (XAS), angle resolved x ray photoelectron spectroscopy (ARXPS), x ray magnetic circular dichroism (XMCD), and element-specific hysteresis loops. The XAS demonstrates a multiplet structure at the Co L3 edge which could be attributed to the formation of CoO at the interface due to the high annealing temperature. The XMCD sum-rule analysis and the element-specific hysteresis loops show a higher magnetic moment, a change in the loop shape, and an increase in the Co coercive field when probing more close to the interface layer. The chemical and structural disorder at the interface has been further revealed by the ARXPS measurements.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.