Abstract
Interfacial reactions between Sn, Sn-3.0 wt.%Ag-0.5 wt.%Cu (SAC), and Sn-9 wt.%Zn (SZ) lead-free solders and Fe-42 wt.%Ni (alloy 42) substrates at 240°C, 255°C, and 270°C were investigated in this study. FeSn2, (Fe,Ni, Cu)Sn2, and (Ni,Fe)5Zn21 phases were formed, respectively, at the interface in the Sn/alloy 42, SAC/alloy 42, and SZ/alloy 42 couples. As the reaction time and temperature were increased, the layered intermetallic compound (IMC) assumed two distinct structures, i.e., a thicker layer and a pillar-shaped IMC, in all couples. The IMC thickness of these couples increased with the increase of reaction time and temperature. The IMC thickness was also proportional to the square root of the reaction time. The interfacial reaction mechanism of these couples was diffusion controlled.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.