Abstract
Diffusion bonding of titanium (Ti) to 17-4 PH high strength stainless steel is challenging owing to the formation of brittle Ti-Fe intermetallic compounds (IMCs) at joint interface. In the current study, it was demonstrated that such detrimental Ti-Fe IMCs can be effectively eradicated by using a silver (Ag) interlayer. The diffusion bonded Ti/Ag/17-4 PH stainless steel is characterized by Ti-Ag solid solution, TiAg, remnant Ag interlayer and Ag-(Fe, Cr, Ni) interdiffusion layer. The interfacial reaction phase TiAg exhibited no detrimental effect on bonding strength. During tensile test, ductile fracture took place in the remaining Ag interlayer of resultant joint. Bonding strength up to ∼420 MPa was obtained over bonding durations in the range of 15 ∼ 25 min. It is thus concluded that using an Ag interlayer is highly appealing in improving bonding strength of diffusion bonded Ti/17-4 PH stainless steel dissimilar joint.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.