Abstract
Ti-16.5Zr-13.5Cu-8.5Ni (wt.%) as a filler and brazing process as 950 °C/60 min were supplied in this study for brazing cast TiAl alloys with fully lamella structure. The interface microstructure and element diffusion were analyzed and measured by SEM, EBSD, and EPAM. And the mechanical properties of joints were evaluated. The sound joints were achieved with strength as 575 MPa at room temperature and remained as 410 MPa and 385 MPa in average at 700 °C and 760 °C, respectively. It was attributed to lots of fine grains with soft orientation as BCC [120] in the joint to the tensile direction. It was found that the fracture happened in the local zones with very large grains and the extreme misorientation between grains in the joint. Even though most grains as Ti3Al phase were found in the joint, there was no sign indicating the formed IMC related to the fracture.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.