Abstract
The CVD nano-diamond film and Ti-6Al-4V alloy were successfully brazed with AgCuTi active brazing filler. The interfacial microstructure was investigated by SEM, EDS, XRD and TEM. Typical interfacial microstructure of brazed joint was conformed as Ti-6Al-4V/diffusion layer/Ti2Cu+TiCu+Ti3Cu4/Ag(s,s)+Cu(s,s)+Ti2Cu3/TiCu+TiC/nano-diamond film. The effects of brazing temperature on interfacial microstructure and mechanical properties of the brazed joints were analyzed. With the increasing brazing temperature, the thickness of reaction layers adjacent to Ti-6Al-4V substrate and nano-diamond film increased obviously. Moreover, the Ti2Cu3 phase coarsened and aggregated in brazing seam at higher temperature. The joint was formed by the diffusion and reactions between atoms, and the microstructure evolution of brazed joint was discussed. In addition, a slight graphitization of nano-diamond film occurred during brazing process, and the highest shear strength can reach 25MPa when the joint was brazed at 880°C for 10min. Finally, the fracture positions and fractographs of brazed joints were also discussed.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.