Abstract
The interfacial reaction between Sn/Au bumps and a thin Au/TiW metallization was investigated. It was found that for 60 μm bumps, the pad metallization was not reliable and large voids were generated after multiple reflow cycles due to the dewetting between eutectic AuSn and TiW. For 40 and 20 μm bumps, the Au/TiW was quite stable and the joints could be entirely composed of TiW/Au5Sn/Au because of the wetting on the side walls of the Au socket.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.