Abstract
AbstractIn this paper, the interface debonding and slipping of carbon fiber-reinforced ceramic-matrix composites (CMCs) subjected to different fatigue loading sequences have been investigated using the micromechanics approach. There are two different types of fatigue loading sequences considered: (1) cyclic loading under low peak stress for N1 cycles, and then high peak stress for N2 cycles; and (2) cyclic loading under high peak stress for N1 cycles, and then low peak stress for N2 cycles. Based on the fatigue damage mechanism of fiber slipping relative to matrix upon unloading/reloading, the interface debonded and slip lengths are determined by fracture mechanics approach. The relationships between interface debonding, interface slipping, interface wear, cycle number, fatigue peak stress, and fatigue loading sequence have been determined. The effects of peak stress level, interface wear, cycle number, and loading sequence on the interface debonding and slipping of fiber-reinforced CMCs have been analyze...
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.