Solid nanocomposite electrolytes (nano-SCEs) that exhibit higher ionic conductivity than the individual confined electrolyte were investigated for high-performance solid-state batteries. Understanding the behavior of Li-ion conduction through the pores is important to design ideal nanoporous structures for nano-SCEs, which are composed of an ionic liquid electrolyte (ILE) in a highly porous (∼90%) silica matrix. To establish the relationship between the pore structure of the silica matrix and the ionic conductivity of the solid nanocomposite, the liquid electrolyte fraction was successfully extracted from the nano-SCE to reveal the fragile porous silica matrix. A careful drying using the CO2 supercritical drying method helps in sustaining the original structure, preventing its collapse due to surface tension. The pore size distribution, Brunauer-Emmett-Teller (BET) surface area, and porosity were characterized using scanning electron microscopy, transmission electron microscopy, and N2 adsorption/desorption techniques. Our results revealed a wide size distribution of macropores and mesopores in the silica matrix. The pore size increased and the effective surface area decreased with increasing ILE/SiO2 molar ratio. The interface conductivity enhancement was found to increase with the thickness of the adsorbed (ice-like) bound-water layer on the silica surface, confirming that the strong hydrogen bonding of the adsorbed ionic liquid molecules on the bound-water layer causes the conduction promotion effect in the nano-SCE. In addition, a large number of small pores lead to a severe pore confinement effect that results in a decreased conductivity due to the increasing viscosity of the ILE filling the pores. The conductivity can be improved by realizing a nano-SCE with an optimized pore size to minimize the pore confinement effect.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.