Abstract
All-solid-state batteries based on a Li metal anode represent a promising next-generation energy storage system, but are currently limited by low current density and short cycle life. Further research to improve the Li metal anode is impeded by the lack of understanding in its failure mechanisms at lithium-solid interfaces, in particular, the fundamental atomistic processes responsible for interface failure. Here, using large-scale molecular dynamics simulations, the first atomistic modeling study of lithium stripping and plating on a solid electrolyte is performed by explicitly considering key fundamental atomistic processes and interface atomistic structures. In the simulations, the interface failure initiated with the formation of nano-sized pores, and how interface structures, lithium diffusion, adhesion energy, and applied pressure affect interface failure during Li cycling are observed. By systematically varying the parameters of solid-state lithium cells in the simulations, the parameter space of applied pressures and interfacial adhesion energies that inhibit interface failure during cycling are mapped to guide selection of solid-state cells. This study establishes the atomistic modeling for Li stripping and plating, and predicts optimal solid interfaces and new strategies for the future research and development of solid-state Li-metal batteries.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.