Abstract
Rutherford backscattering/channeling (RBS/C) and X-ray diffraction (XRD) are used to comprehensively characterize a heterostructure of AlInGaN/GaN/Al2O3(0001). The AlInGaN quaternary layer was revealed to process a high crystalline quality with a minimum yield of 1.4% from RBS/C measurements. The channeling spectrum of (1 (2) under bar 13) exhibits higher dechanneling than that of (0001) at the interface of AlInGaN/GaN. XRD measurements prove a coherent growth of AlInGaN on the GaN template layer. Combining RBS/C and XRD measurements, we found that the interface of GaN/Al2O3 is a nucleation layer, composed of a large amount of disorders and cubic GaN slabs, while the interface of AlInGaN/GaN is free of extra disordering (i.e. compare with the GaN layer). The conclusion is further evidenced by transmission electron microscopy (TEM). (c) 2005 Elsevier Ltd. All rights reserved.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.