Abstract
TiAl and 42CrMo steel were vacuum brazed with Ag–Cu/Ti/Ag–Cu filler metal. The joint interface was divided into three distinct zones, including the reaction layer near TiAl, the central zone, and the TiC reaction layer adjacent to the steel. During brazing, AlCu2Ti, AlCuTi and TiC phase formed quickly with an increase in brazing temperature or brazing time. By comparing the brazing conditions and joint strengths, the optimum brazing parameters were obtained. When brazed at 900 °C for 5 min, the room temperature tensile strength and shear strength of the joint were 347 MPa and 229 MPa, respectively.
Published Version
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.