Abstract
In order to investigate interfacial characteristics between top-Au and pentacene layers, devices with the structure of bottom-Au/pentacene/top-Au were fabricated on glass substrates at various deposition rates of top-Au of about 1.0, 3.0 and 15.0 Å/s. It was observed that electrical characteristics could be improved by increasing the deposition rate of top-Au, and the highest electrical conductivity value, 1.5×10-6 S/cm, was obtained for the device with top-Au deposited at 15.0 Å/s. Auger electron spectroscopy (AES) results showed that the atomic content of Au is substantially increased with the deposition rate of top-Au, but there is no marked difference in the depth profile of Au atoms regardless of the deposition rate of top-Au. Likewise, field-emission scanning electron microscopy (FE-SEM) images did not reveal structural defects that might cause short circuit. We also fabricated top-contact organic thin-film transistors (OTFTs) at various deposition rates of the Au layer for source/drain electrodes. As a result, the performance of the OTFTs can be modified by the deposition rate of Au. These results will be discussed.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.