Abstract
Gold (Au) and silver (Ag) are known to be important contact metals on YBa2Cu3O7−x (YBCO). Both metals have been used as additives in fabricating tapes of YBCO and Bi2Sr2CaCu2O8 (BSCCO) materials, and have favorable results in improving not only the flexibility but also the weighted critical currents of the resulting composites. Previous results on superconductor/normal metal/superconductor junctions made using YBCO/Au/YBCO and YBCO/Au/Nb demonstrated that a supercurrent can be induced in the normal metal layers through the proximity effect. Our transmission electron microscopy study of the Au/YBCO interfaces shows a well-bonded interface with no extraneous phases present. Lattice fringes of the (001) plane in YBCO terminated at the interface abruptly. This observation supports previous results of contact resistance of x-ray photoelectron spectroscopy (XPS). Both (001) integral steps and multiples of 1/3 (001) steps were observed at the Au/YBCO interface. When the top gold layer was absent locally, surface degradation was observed as the (001) lattice fringes stopped short from the surface by 10 nm. Our results support that Au is a desirable contact metal and a dependable surface passivation material for YBCO.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.