Abstract
Interdiffusion study is conducted in the Ni-Zr system in the temperature range of 750-850 A degrees C. Five intermetallic compounds, Ni5Zr, Ni7Zr2, Ni10Zr7, NiZr and NiZr2 are found to grow in the interdiffusion zone. Integrated diffusion coefficients are estimated for different phases. Activation energy is found to be lowest for Ni10Zr7 (178 +/- A 8 kJ/mol) and highest for NiZr (323 +/- A 6 kJ/mol). Tracer diffusion coefficients are estimated at the location of the Kirkendall marker plane in the Ni7Zr2 phase. Ni is found to have 10 times higher diffusion rate compared to Zr in this phase. Higher diffusion rate of Ni compared to Zr is found, which is expected because of higher number of Ni-Ni bonds compared to Zr-Zr bonds in this phase.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.