Abstract
Interdiffusion in the Fe2O3-TiO2 system was investigated by the diffusion couple method in the temperature range of 1323 to 1473 K. The diffusion concentration curves of Ti4+ cations were obtained by electron probe microanalysis, according to which the Boltzmann-Matano method optimized by Broeder was used to calculate the interdiffusion coefficients. The interdiffusion coefficients almost increased linearly with the mole fraction of Ti4+ cations increasing, and they were in the range of 10−12–10−11cm2·s−1. The increase of temperature could also lead to the increase of the interdiffusion coefficients at a constant concentration of Ti4+ cations. It was also found that the thickness growth of the diffusion layer obeyed the parabolic rate law.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
More From: International Journal of Minerals, Metallurgy, and Materials
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.