Abstract
AbstractThe creep properties of fully lamellar γ/α2 titanium aluminides can be significantly improved by alloying with Nb, Ta or Zr. While the influence of these alloying elements on the γ-phase has already been examined, their diffusivity and strengthening properties in the α2-phase are still lacking. In order to study the effect of Nb, Ta and Zr in α2-Ti3Al, the alloys Ti-33Al, Ti-33Al-5Nb, Ti-33Al-5Ta and Ti-33Al-5Zr were investigated using a diffusion couple approach and strain rate jump tests. The results show that Zr diffuses the fastest, followed by Nb and Ta. Furthermore, these alloying elements also increase the strength compared to a binary Ti-33Al alloy, from which Zr leads to the highest strength increase followed by Ta and Nb. The lower diffusivity of Ta becomes increasingly important at higher temperatures and lower strain rates resulting in a higher strengthening potential than Nb and Zr under such conditions.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.