Abstract
The interaction of an Fe–Al–Cr–C (29.5 wt % Fe, 29.35 wt % Cr, 2.56 wt % C, 38.59 wt % Al) alloy with the melt of a lithium, sodium, or potassium carbonate containing 1–5 wt % addition to a salt phase is studied by gravimetry and measuring the corrosion potential and anode polarization curves in the temperature range 500–600°C. As passivators, the substances that decrease the corrosion losses due to hardening and thickening of an oxide film (lithium, sodium, potassium hydroxides) are used. As corrosion stimulators (activators), sodium chloride, fluoride, and sulfate are used. The coalloying of iron with chromium and aluminum results in high corrosion resistance against both frontal (continuous) and local (pitting, intercrystalline) corrosion as a result of formation of chemically resistant and high-adhesion oxide layers with their participation. X-ray diffraction analysis reveals gamma aluminum oxide, spinel (alumochromite) traces, and lithium aluminate at the surface.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.