Abstract
An integration technology for wafer-level LiNbO3 single-crystal thin film on Si has been achieved. The optimized spin-coating speed of PI (polyimide) adhesive is 3500 rad/min. According to Fourier infrared analysis of the chemical state of the film baked under different conditions, a high-quality PI film that can be used for wafer-level bonding is obtained. A high bonding strength of 11.38 MPa is obtained by a tensile machine. The bonding interface is uniform, completed and non-porous. After the PI adhesive bonding process, the LiNbO3 single-crystal was lapped by chemical mechanical polishing. The thickness of the 100 mm diameter LiNbO3 can be decreased from 500 to 10 μm without generating serious cracks. A defect-free and tight bonding interface was confirmed by scanning electron microscopy. X-ray diffraction results show that the prepared LiNbO3 single-crystal thin film has a highly crystalline quality. Heterogeneous integration of LiNbO3 single-crystal thin film on Si is of great significance to the fabrication of MEMS devices for in-situ measurement of space-sensing signals.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.