Abstract
For the first time, the potentially cost-effective technologies of rapid thermal processing (RTP) and screen-printing (SP) have been combined into a single process sequence to achieve solar cell efficiencies as high as 14.7% on 0.2 /spl Omega/-cm FZ and 14.8% on 3 /spl Omega/-cm Cz silicon. These results were achieved without application of a nonhomogeneous (selective) emitter, texturing, or oxide passivation. By tailoring the RTP thermal cycles for emitter diffusion and firing of the screen-printed silver contacts, fill factor values >0.79 were realized on emitters with a sheet resistance (/spl rho//sub s/) of /spl sim/20 /spl Omega///spl square/ and grid shading <6%. Such high fill factors clearly demonstrate that screen-printed contacts can be fired on extremely shallow RTP emitters (x/sub j/=0.25-0.3 μm) without shunting cells. IQE analysis depicts a strong preference for shallow emitter junction depths to achieve optimal short wavelength response of these unpassivated emitters. In some cases, front contacts were printed through plasma enhanced chemical vapor deposited (PECVD) SiN/SiO <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</sub> dielectrics which prevented the shunting of shallow emitters by serving as partial barriers minimizing the diffusion of metallic species from the contacts. The firing of screen-printed contacts through these PECVD films, achieved the multiple purposes of contact formation, efficient front surface passivation due to annealing of the SiN, and high quality antireflection (AR). Research is presently underway to further optimize the RTP emitter design for screen-printing and develop techniques for implementing selective emitter and oxide passivation technologies for higher efficiency cells.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.