Abstract
AbstractAmorphous tungsten nitride (WNx) is a promising diffusion barrier for extending Cu metallization beyond 0.18 μm. This study evaluates the barrier performance, adhesion, and step coverage of PECVD WN 0.5 integrated with a CVD Cu seed layer. The WN0.5 films exhibit amorphous structure with 33% bottom and side-wall step coverage in 0.14 μm wide structures with 9:1 aspect ratio. The potential of 50 Å WN0.5 as an effective Cu barrier is shown by the absence of Secco etch-pits in the Si substrate after a 30 min anneal at 500°C. When deposited on PECVD WN0.5 the CVD Cu films exhibit uniform nucleation, and as deposited resistivity of 2.5 μΩ-cm. Step coverage of the CVD Cu is better than 95% in 0.14 μm structures. Adhesion exceeding epoxy strength of the CVD Cu seed layer even to air-exposed WN0.5 is demonstrated using stud-pull adhesion tests.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.