Integrated vapor pressure, hygroswelling, and thermo-mechanical stress modeling of QFN package during reflow with interfacial fracture mechanics analysis

Abstract

In this paper, a comprehensive and integrated package stress model is established for quad flat non-lead package with detailed considerations of effects of moisture diffusion, heat transfer, thermo-mechanical stress, hygro-mechanical stress and vapor pressure induced during reflow. The critical plastic materials, i.e., moldcompound and die attach are characterized for hygroswelling and moisture properties, which are not easily available from material suppliers. The moisture absorption during preconditioning at JEDEC Level 1, and moisture desorption at various high temperatures are characterized. The moisture diffusivity is a few orders higher at reflow temperature than moisture preconditioning temperature. Due to coefficient of moisture expansion mismatch among various materials, hygro-mechanical stress is induced. The concept is analogous to coefficient of thermal expansion mismatch which results in thermo-mechanical stress. Thermal diffusivity is much faster than the moisture diffusivity. During reflow, the internal package reaches uniform temperature within a few seconds. The vapor pressure can be calculated based on the local moisture concentration after preconditioning. Results show that the vapor pressure saturates much faster than the moisture diffusion, and a near uniform vapor pressure is reached in the package. The vapor pressure introduces additional strain of the same order as the thermal strain and hygrostrain to the package. Subsequently, the interfacial fracture mechanics model is applied to study the effect of crack length on die/mold compound and die/die attach delamination.