Integral-breadth analysis of X-ray line broadening in cold-worked natural molybdenite (MoS2) crystals

Abstract

An anomalous X-ray line broadening effect has been studied in cold-worked natural molybdenite (MoS2)crystals using the integral-breadth method. The stacking-fault probability is calculated on the basis of simple h.c.p. structure and is found to be approximately 0.03 on taking account the glide on S–S (sulphur–sulphur) slip planes only. Also, lattice strain and domain-size parameter have been estimated. The dislocation density calculated from the domain-size is found to be ≈2.6 × 1010 cm/cm3. A justification for using the simple h.c.p. structure theory for molybdenite has also been given. Ein anomaler Röntgenlinienverbreiterungseffekt wurde an kaltbearbeiteten, natürlichen Molybdänit (MoS2)-Kristallen mittels einer Integral-“breadth”-Methode untersucht. Die Stapelfehlerwahrscheinlichkeit wird auf der Grundlage einer simplen h.d.p.-Struktur berechnet und gefunden, daß sie näherungsweise 0,03 beträgt, wobei allein Gleitung auf S–S (Schwefel–Schwefel)-Gleitebenen berücksichtigt wird. Gitterdehnung und Domänen-größeparameter wurden ebenfalls berechnet. Die Versetzungsdichte wurde aus der Domänengröße zu ≈2,6 × 1010 cm/cm3 bestimmt. Eine Rechtfertigung für die Benutzung der einfachen h.d.p.-Strukturtheorie für Molybdänit wird ebenfalls angegeben.