Insights into thermal diffusion of germanium and oxygen atoms in HfO2/GeO2/Ge gate stacks and their suppressed reaction with atomically thin AlOx interlayers

Abstract

The thermal diffusion of germanium and oxygen atoms in HfO2/GeO2/Ge gate stacks was comprehensively evaluated by x-ray photoelectron spectroscopy and secondary ion mass spectrometry combined with an isotopic labeling technique. It was found that 18O-tracers composing the GeO2 underlayers diffuse within the HfO2 overlayers based on Fick's law with the low activation energy of about 0.5 eV. Although out-diffusion of the germanium atoms through HfO2 also proceeded at the low temperatures of around 200 °C, the diffusing germanium atoms preferentially segregated on the HfO2 surfaces, and the reaction was further enhanced at high temperatures with the assistance of GeO desorption. A technique to insert atomically thin AlOx interlayers between the HfO2 and GeO2 layers was proven to effectively suppress both of these independent germanium and oxygen intermixing reactions in the gate stacks.