Abstract
This paper demonstrates the changes in the nanoscale morphology of the blended films induced by a diffusion of C60 molecules and degradation during longer thermal treatment above the glass transition temperature (130 °C). The results showed that the film morphology, including the size and population of poly(3-hexylthiophene) (P3HT) crystallites, rapidly reduced with annealing time. A large-scale (>1μm) C60 aggregation, demonstrating a bulky phase separation between the polymer and C60, was identified after 5 h annealing, which resulted in a degradation of charge carrier mobility and conductivity. X-ray diffraction verifies that the interchain packing of P3HT within the crystallized phase improved with an increasing in annealing time, but the volume fraction of the P3HT (100) phase normal to substrate increased up to 3 h and decreased at longer annealing times resulting in the ageing of the films. Changes in the infrared spectra of the extended annealed samples were recorded and the oxidation products were identified. A degradation mechanism that accounted for the modifications in the infrared spectra and a detachment of the hexyl chain from P3HT was demonstrated, resulting in chain cutting, conjugation loss and a reduction in the UV–vis absorbance. The morphology change with the annealing time resulted in an abrupt decrease in the PCE of P3HT:C60 solar cells. These findings signify that the stability of P3HT:C60 solar cells cannot be secured for longer annealing period owing to the unsettled morphology.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.