Abstract
The arc torch angle greatly affected the deposition characteristics in the wire arc additive manufacturing (WAAM) process, and the relation between the droplet transition behavior and macrostructure morphology was unclear. This work researched the effect of torch angle on the formation accuracy, droplet transition behavior and the mechanical properties in the WAAM process on a ZL205A aluminum alloy. The results suggested that at the obtuse torch angle, part of the energy input was used to heat the existing molten pool, which was optimized for the longer solidification period of the molten pool. Therefore, the greater layer penetration depth at 100° resulted in the improved layer-by-layer combination ability. The obtuse torch angle was associated with the better formation accuracy on the sidewall surface due to the smaller impact on the molten pool, which was influenced by both the arc pressure and droplet impact force. The eliminated pores were optimized for the mechanical properties of depositions at a torch angle of 100°; thus, the tensile strength and elongation attained maximum values of 258.6 MPa and 17.1%, respectively. These aspects made WAAM an attractive mode for manufacturing large structural components on ZL205A aluminum alloy.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Similar Papers
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.